Monoazo metal complex compound containing composition and production method thereof

ABSTRACT

Monoazo metal complex compound containing composition, the incidence of skin sensitization in a skin sensitization potential test based on the maximization method of said composition being not more than 20% and method for producing said composition which comprises a step for removing impurity substances using an alcoholic organic solvent; charge control agent comprising said composition and toner containing said charge control agent; coloring agent containing said composition and colored thermoplastic resin composition containing said coloring agent.

BACKGROUND OF THE INVENTION

[0001] 1. Field of the Invention

[0002] The present invention relates to a monoazo metal complex compoundcontaining composition exhibiting almost no skin sensitizationpotential, a production method therefor, a charge control agentcomprising the monoazo metal complex compound containing composition, atoner for developing electrostatic images that contains the chargecontrol agent, a coloring agent containing said monoazo metal complexcompound containing composition, and a colored thermoplastic compositioncontaining said monoazo metal complex compound containing composition asa coloring agent.

[0003] 2. Description of the Prior Art

[0004] Skin sensitization is a contact allergic reaction induced by skincontact with a simple chemical substance, a metal, or the like, and is aform of skin allergy (e.g., allergic contact dermatitis). The termallergy is defined as an inflammation reaction due to antibodyproduction by the living body. Sensitization refers to the entry of anantigen in the living body to cause an antibody to be produced. Inrecent years, an emphasis has been placed on the potential of compoundsfor inducing skin sensitization in view of their safety.

[0005] Examples of reported cases wherein the safety of chemicalsubstances posed a problem include a case of a chlorinated phosgenecompound produced from a reaction of sodium hypochlorite and a yellowdye in a DC brand sweater [Hifu/Skin 1989;31(Supple. 7):24-33], a caseof the grounder naphthol AS remaining on cloth in a cotton flannel nightclothes [Eiseikagaku/Journal of Hygienic Chemistry 1986;32(5):359-67], acase of the grounder naphthol AS-D remaining on cloth in a cottonflannel night clothes [Environ. Dermatol. 1995;2:278-82], a case ofDisperse Red 153, Disperse Blue 106, and Disperse Blue 124 in one-piecedress [Contact Dermatitis 1996;34:6-11], a case of the azo disperse dyesDisperse Yellow 3, Disperse Orange 3, and Disperse Red 17 formulated ascoloring agents in plastic eyeglass frames [Environmental Dermatology1994; 1(Supple. 1):50], and a case of Solvent Orange 60 formulated as acoloring agent in plastic eyeglass frames [Environmental Dermatology1998;5(Supple. 1):92]. As the demand for regulation of the skinsensitization potential of compounds is increasing, it is of paramountimportance from the viewpoint of safety to assess the allergic reactionof new chemicals and newly launched commercial products.

[0006] For determining the sensitizing potential of such chemicals,there have been proposed new methods, including the Beuhler test method,which simulates actual use in the human body, and the maximizationmethod, which determines the potential of the test compound. As a resultof the meeting of experts of the Organization for Economic Cooperationand Development/OECD held in May of 1991, the OECD guidelines werepresented, in which priority is given to the Beuhler test method and themaximization test of Magnusson and Kligman using the guinea pig(maximization test method).

[0007] Monoazo metal complex compounds are used for variousapplications, occupying an important position in the industry. Majorapplications include dyes used to impart colors for writing inks,recording inks (including inkjet inks), leather, plastics, etc.;coloring matters based on absorption of ultraviolet light, near infraredlight, infrared light, etc.; and charge control or enhancement agentsused in toners for developing electrostatic images and resin powderpaints for electrostatic painting.

[0008] These applications of monoazo metal complex compounds all callfor consideration of effects on the human body and the environment, inaddition to the performance required for the applications. In the caseof monoazo metal complex compounds as charge control agents, forexample, their effects on the human body and the environment ascompounds, as well as their charge characteristics, must be taken intoconsideration.

[0009] Regarding effects on the human body, skin sensitization potentialtests for compounds provide an especially important set of safety data.In recent years, priority has often been given to assessment of skinsensitization potential based on the aforementioned maximization method.

[0010] However, because of the production method, monoazo metal complexcompounds have impurity substances from starting materials, andbyproducts and impurity substances associated with metallization,resulting in problems to be solved in skin sensitization assessed usingthe maximization method.

[0011] Accordingly, the object of the present invention is to provide amonoazo metal complex compound containing composition characterized byhigh safety to the human body and a low incidence of skin sensitizationin skin sensitization tests, especially the maximization method, aproduction method therefor, a charge control agent comprising themonoazo metal complex compound containing composition, a toner fordeveloping electrostatic images that contains the charge control agent,a coloring agent containing said monoazo metal complex compoundcontaining composition, and a colored thermoplastic compositioncontaining the monoazo metal complex compound containing composition asa coloring agent.

SUMMARY OF THE INVENTION

[0012] The monoazo metal complex compound containing composition of thepresent invention contains a monoazo metal complex compound, theincidence of skin sensitization in a skin sensitization potential test,especially in a skin sensitization potential test based on themaximization method, of said composition being not more than 20%.

[0013] This monoazo metal complex compound containing composition isdesirably such that the purity of the aforementioned monoazo metalcomplex compound is not less than 90% as determined by high performanceliquid chromatography.

[0014] The production method of the present invention for a monoazometal complex compound containing composition is a method for producingthe aforementioned monoazo metal complex compound containing compositionand comprises a step for removing impurity substances using an alcoholicorganic solvent.

[0015] By comprising a step for removing impurity substances using analcoholic organic solvent to obtain a composition containing a monoazometal complex compound at high purity, the incidence of skinsensitization in skin sensitization potential tests based on themaximization method can be reduced to not more than 20%.

[0016] The charge control agent of the present invention comprises theaforementioned monoazo metal complex compound containing composition,and the toner of the present invention for developing electrostaticimages contains this charge control agent.

[0017] The coloring agent of the present invention contains theaforementioned monoazo metal complex compound containing composition,and the colored thermoplastic resin composition of the present inventioncontains the aforementioned monoazo metal complex compound containingcomposition as a coloring agent.

[0018] The monoazo metal complex compound containing composition of thepresent invention possesses good characteristics of monoazo metalcomplex compounds and is excellently safe to the human body with theincidence of skin sensitization in skin sensitization potential tests,especially in a skin sensitization potential test based on themaximization method, being not more than 20%. The monoazo metal complexcompound containing composition of the present invention can be producedusing the production method of the present invention.

[0019] The charge control agent of the present invention is excellentlysafe to the human body with the ratio of guinea pigs with skinsensitization signs found in skin sensitization potential tests,especially in a skin sensitization potential test based on themaximization method, being not more than 20%, possesses a practicallysatisfactory charge characteristic. In addition, because the chargecontrol agent of the present invention is of high purity with impuritysubstances removed previously, it is sharp in charge amountdistribution, high in charge amount uniformity, excellent in charge riseprofile, low in environmental dependency, and when used in toner, it isexcellent in durability in multiple repeated use of toner, and does notadversely affect toner fixability and offset quality.

[0020] Because the toner of the present invention for developingelectrostatic images contains the charge control agent of the presentinvention, it is excellently safe to the human body, possesses apractically satisfactory charge characteristic, is sharp in chargeamount distribution, high in charge amount uniformity, excellent incharge rise profile, low in environmental dependency, excellent indurability in multiple repeated use, and good in fixability and offsetquality.

[0021] The coloring agent of the present invention is excellently safeto the human body with the ratio of guinea pigs with skin sensitizationsigns found in skin sensitization potential tests, especially in a skinsensitization potential test based on the maximization method, being notmore than 20%, possesses a practically satisfactory coloringcharacteristic. In addition, because the coloring agent of the presentinvention is of high purity with impurity substances removed previously,its solubility is very stable, it exhibits almost no transfer, such asbleeding due to impurity substances, its heat resistance and lightfastness are excellent, and its fading is slow with almost no hue changeduring color fading.

[0022] Because the colored thermoplastic resin composition of thepresent invention contains as a coloring agent a monoazo metal complexcompound containing composition that is excellently safe to the humanbody, is of high purity, and is good in dispersibility and/or solubilityin thermoplastic resins, it is excellent in uniform colorability, lightfastness, and heat resistance, and provides molded products withimproved gloss and appearance.

BRIEF DESCRIPTION OF THE DRAWINGS

[0023]FIG. 1 shows high performance liquid chromatography data for themonoazo metal complex compound obtained in Example 1.

[0024]FIG. 2 shows a TG/DTA chart of the monoazo metal complex compoundobtained in Example 1.

[0025]FIG. 3 shows high performance liquid chromatography data for themonoazo metal complex compound obtained in Comparative Example 1.

[0026]FIG. 4 shows high performance liquid chromatography data for themonoazo metal complex compound obtained in Comparative Example 2.

[0027]FIG. 5 shows a TG/DTA chart of the monoazo metal complex compoundobtained in Comparative Example 2.

[0028]FIG. 6 shows changes in the charge amounts of the toners ofExamples 3 and 4 and Comparative Examples 3 and 4.

DETAILED DESCRIPTION OF THE INVENTION

[0029] The monoazo metal complex compound containing composition(generally referred to as “monoazo metal complex compound”) of thepresent invention is characterized in that the incidence of skinsensitization in skin sensitization potential tests, especially in askin sensitization potential test based on the maximization method, isnot more than 20%.

[0030] The monoazo metal complex compound containing composition of thepresent invention possesses characteristics comparable to those ofcommercially available conventional monoazo metal complex compounds andcan be used equivalently. In addition, it does not significantly affectthe human body with a low incidence of skin sensitization in skinsensitization potential tests, especially in a skin sensitizationpotential test based on the maximization method.

[0031] Skin sensitization tests that can be used for the presentinvention include skin sensitization tests using adjuvants, such as themaximization test, the adjuvant and strip test, Freund's completeadjuvant test, the optimization test, and the split adjuvant test; andskin sensitization tests using no adjuvant, such as the Beuhler test,the Draize test, and the open epicutaneous test. In addition, in thepresent invention, skin sensitization tests and simplified test methodsbased on the aforementioned test methods are also applicable. Providinghigh accuracy of sensitization measurement, the maximization test(maximization method) is particularly preferable.

[0032] In addition, in recent years, there has been a trend for theabolishment of in vivo experimental methods in association with thespirit of animal welfare. Accordingly, in vitro methods for skinsensitization potential tests, such as the local lymphonode assay (LLA),have been developed. Although a problem remains to be solved that all invitro methods are lower than the maximization method in terms of thepower of detection, it is expected that advances such as improvement inthe power of detection will be achieved, and that in vitro methods willconstitute the mainstream of skin sensitization potential tests. Assuch, skin sensitization tests are also applicable to the presentinvention.

[0033] A skin sensitization test based on the maximization method cantypically be performed as described below. To one previously clippedshoulder of a guinea pig, a 1:1 mixture of Freund's complete adjuvant(immunopotentiator) and the test compound is injected intracutaneouslyfor first induction. For second induction, 5% sodium lauryl sulfate(petrolatum base) is applied in an open state to increase the absorptionof the test compound 7 days after the intracutaneous injection and isremoved after 24 hours. The test compound is then applied in a closedstate to the open application site and removed after 48 hours. Two weeksafter closed application of the test compound, the test compound isagain applied to elicit the skin reaction; after 24 hours, the testcompound is removed and the skin reaction status is examined. At least10 guinea pigs are used for the treatment group and at least 5 for thecontrol group; rating results are expressed as the ratio of guinea pigswith signs of skin sensitization by the test compound.

[0034] The production method of the present invention for a monoazometal complex compound containing composition (generally referred to as“monoazo metal complex compound”) can comprise a step for removingimpurity substances other than monoazo metal complex compounds using analcoholic organic solvent, in, for example, the synthesis of a monoazometal complex compound, or the purification of a monoazo metal complexcompound.

[0035] Examples of the step for removing impurity substances other thanmonoazo metal complex compounds using an alcoholic organic solventinclude, but are not limited to, the following.

[0036] (1) The monoazo metal complex compound containing composition isdispersed in an alcoholic organic solvent; the resulting dispersion isstirred under heating and filtered, after which the cake filtered out isdried under reduced pressure.

[0037] (2) After impurity substances are removed from the monoazo metalcomplex compound containing composition by thermally refluxing analcoholic organic solvent using the soxhlet extractor, either themonoazo metal complex compound containing composition is dried underreduced pressure or the alcoholic organic solvent in the wet cake isreplaced with water, followed by drying with a warm wind.

[0038] (3) A monoazo metal compound is synthesized in a non-alcoholicsolvent and after the non-alcohol solvent is replaced with an alcoholicorganic solvent, impurity substances are removed by filtration etc.,followed by drying. For example, a monoazo metal compound is synthesizedin an aqueous system and filtered, and the water in the thus-obtainedwet cake is replaced with an alcoholic organic solvent, followed bydrying with a warm wind.

[0039] (4) A monoazo metal compound is synthesized in an alcoholicorganic solvent, and impurity substances are removed by filtration etc.,followed by drying.

[0040] Alcoholic organic solvents that can be used for the productionmethod of the present invention for a monoazo metal complex compoundcontaining composition include, for example, the following monohydricalcohols, polyhydric alcohols (glycols) and derivatives thereof andmixtures of two or more thereof. Specifically, there may be mentionedalcohols such as methanol, ethanol, 1-propanol, 2-propanol, n-butanol,benzyl alcohol, 1-octanol, 2-octanol, and α-methylbenzyl alcohol, orderivatives thereof; and glycols such as ethylene glycol, diethyleneglycol, propylene glycol, hexylene glycol, benzyl glycol, ethyleneglycol monodibutyl ether, ethylene glycol monophenyl ether (phenylglycol), diethylene glycol monoethyl ether, diethylene glycol monomethylether, diethylene glycol monobutyl ether, diethylene glycol dibutylether, diethylene glycol monophenyl ether, propylene glycol monobutylether, propylene glycol monophenyl ether, dipropylene glycol monomethylether, dipropylene glycol monoethyl ether, dipropylene glycol monobutylether, dipropylene glycol monophenyl ether, tripropylene glycolmonomethyl ether, tripropylene glycol monoethyl ether, diethylene glycolmonoethyl ether acetate, propylene glycol monomethyl ether acetate, andpropylene glycol diacetate, or derivatives thereof. Preference is givento one member or a mixture of two or more members selected from thegroup consisting of methanol, ethanol, 1-propanol, 2-propanol,n-butanol, ethylene glycol, propylene glycol monomethyl ether, andethylene glycol monoethyl ether.

[0041] The monoazo metal complex compound containing composition of thepresent invention is useful, provided that the monoazo metal complexcompound is a compound of the following formula (1):

[0042] wherein, each of R¹ through R⁴ and R⁶ independently (whetheridentical or not) represents a hydrogen atom, a normal or branched alkylgroup having 1 to 18 carbon atoms (e.g., methyl, ethyl, propyl, butyl,pentyl, hexyl, heptyl, octyl, nonyl, undecyl, dodecyl), a normal orbranched alkenyl group having 2 to 18 carbon atoms (e.g., vinyl,propenyl, butenyl), a sulfonamide group, a mesyl group, a sulfonic acidgroup, a hydroxy group, an alkoxy group having 1 to 18 carbon atoms(e.g., methoxy, ethoxy, propoxy, butoxy, pentyloxy, hexyloxy), anacetylamino group, a benzoylamino group, a halogen atom (e.g., Cl, Br,I), or —COO—R⁷;

[0043] R⁷ represents a normal or branched alkyl group having 1 to 18carbon atoms (e.g., methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl,octyl, nonyl, undecyl, dodecyl) or an aryl group having 6 to 18 carbonatoms (e.g., phenyl, tolyl, xylyl, naphthyl);

[0044] R⁵ represents a hydrogen atom, a halogen atom (e.g., Cl, Br, I),a nitro group, a carboxyl group, a normal or branched alkyl group having1 to 18 carbon atoms (e.g., the same as those mentioned above), analkenyl group having 2 to 18 carbon atoms (e.g., the same as thosementioned above), an alkoxy group having 1 to 18 carbon atoms (e.g., thesame as those mentioned above), an aryl group having 6 to 18 carbonatoms (e.g., the same as those mentioned above), —COO—R⁸ or

[0045] R⁸ represents a normal or branched alkyl group having 1 to 18carbon atoms (e.g., the same as those mentioned above) or an aryl grouphaving 6 to 18 carbon atoms (e.g., the same as those mentioned above);

[0046] Y represents a hydrogen atom, a normal or branched alkyl grouphaving 1 to 8 carbon atoms (e.g., methyl, ethyl, propyl, butyl, pentyl,hexyl, heptyl, octyl), an alkoxy group having 1 to 5 carbon atoms (e.g.,methoxy, ethoxy, propoxy, butoxy, pentyloxy), a nitro group, or ahalogen atom (e.g., the same as those mentioned above);

[0047] m represents an integer from 1 to 3;

[0048] M represents a divalent or trivalent metal (e.g., Cr, Fe, Co, Ni,Cu, Ti, Al);

[0049] p represents 1 or 2;

[0050] (A)^(q+) represents H⁺, NH₄ ⁺, a cation based on an alkali metal(Na, K, or the like), a cation based on an organic amine (aliphaticprimary amine, aliphatic secondary amine, aliphatic tertiary amine, orthe like), or a quaternary organic ammonium ion;

[0051] q represents 1 or 2; and

[0052] X represents 1 or 2.

[0053] The monoazo metal complex compound in the monoazo metal complexcompound containing composition of the present invention is preferablysuch that (A)^(q+) in Formula (1) above is H⁺, whereby impuritysubstances that adversely affect the sensitization potential can beremoved efficiently by controlling the alcohol solubility of the monoazometal complex compound to minimize the loss of the monoazo metal complexcompound.

[0054] In addition, the monoazo metal complex compound in the monoazometal complex compound containing composition of the present inventionis preferably such that R² is Cl;

[0055] each of R¹ and R³ through R⁵ is a hydrogen atom;

[0056] R⁶ is a hydrogen atom or a normal or branched alkyl group having1 to 18 carbon atoms;

[0057] M is Cr, Fe, or Cu; and

[0058] (A)^(q+) is H⁺.

[0059] According to the production method of the present invention for amonoazo metal complex compound containing composition, it is possible toproduce the monoazo metal complex compound containing composition of thepresent invention, while remaining starting materials and impuritysubstances associated with monoazo dyes, byproducts and impuritysubstances associated with metallization of monoazo dyes, and otherundesirable substances are removed efficiently. For example, naphthol ASproducts such as naphthol AS and naphthol AS-D, which are also used ascoupling components of monoazo dyes, described with reference to theprior art above, can be removed so that a monoazo metal complex compoundcontaining composition (generally referred to as “monoazo metal complexcompound”) with almost no sensitizing potential is obtained.

[0060] In addition, the monoazo metal complex compound containingcomposition of the present invention is effective as a charge controlagent. In other words, it serves as a charge control agent such that theincidence of skin sensitization in skin sensitization potential tests,especially in a skin sensitization potential test based on themaximization method, is not more than 20%.

[0061] The charge control agent of the present invention possessescharge characteristics comparable to those of commercially availableconventional charge control agents comprising monoazo metal complexcompounds and can be used equivalently. In addition, it does notsignificantly affect the human body with a low incidence of skinsensitization in skin sensitization potential tests, especially in askin sensitization potential test based on the maximization method.Furthermore, because the monoazo metal complex compound as the chargecontrol agent of the present invention is a monoazo metal complexcompound of high purity with impurity substances removed previously, itis sharper in charge amount distribution, higher in charge amountuniformity, better in charge rise profile (high in charge rise speed),lower in environmental dependency, and when used in toner, it is betterin durability in multiple repeated use of toner, less influential ontoner fixability and offset quality, and better in safety to the humanbody, as compared to commercially available conventional charge controlagents comprising monoazo metal complex compounds.

[0062] The toner of the present invention for developing electrostaticimages can comprise the charge control agent of the present invention, aresin, and a coloring agent.

[0063] The toner of the present invention for developing electrostaticimages can serve well, as long as the charge control agent of thepresent invention is contained in an amount enabling the control of thetoner charge. Preferable amounts of the charge control agent of thepresent invention added are 0.1 to 10 parts by weight, more preferably0.5 to 5 parts by weight, of the aforementioned monoazo metal complexcompound containing composition (charge control agent of the presentinvention), per 100 parts by weight of the resin.

[0064] As examples of resins that can be used for the toner of thepresent invention, there may be mentioned the following resins known astoner resins or binder resins. Specifically, useful resins includestyrene resin, styrene-acrylic resin, styrene-butadiene resin,styrene-maleic acid resin, styrene-vinyl methyl ether resin,styrene-methacrylate copolymer, phenol resin, epoxy resin, polyesterresin, polypropylene resin, and paraffin wax. These resins may be usedsingly or in blends of several kinds.

[0065] The toner of the present invention may incorporate various dyesor pigments as coloring agents. Examples of useful dyes and pigmentsinclude the following. Specifically, there may be mentioned organicpigments such as Quinophthalone Yellow, Isoindolinone Yellow, PerinoneOrange, Perylene Maroon, Rhodamine 6G Lake, Quinacridone Red, RoseBengale, Copper Phthalocyanine Blue, Copper Phthalocyanine Green anddiketopyrrolopyrrole pigments; inorganic pigments such as Carbon Black,Titanium White, Titanium Yellow, Ultramarine, Cobalt Blue and red ironoxide; various oil soluble dyes and disperse dyes such as azo dyes,quinophthalone dyes, anthraquinone dyes, phthalocyanine dyes, indophenoldyes and indoaniline dyes; and triarylmethane dyes and xanthene dyesmodified with resins such as rosin, rosin-modified phenol, androsin-modified maleic acid. These coloring agents may be used singly orin blends of two or more kinds.

[0066] Also, to improve toner quality, additives, e.g.,electroconductive particles, fluidity-improving agents andanti-image-peeling agents, can be added to the toner internally orexternally.

[0067] The toner of the present invention for developing electrostaticimages can, for example, be produced as described below. Specifically, atoner having a mean particle diameter of 1 to 15 μm, for example, can beobtained by thoroughly mixing a resin and a coloring agent as describedabove, and the charge control agent of the present invention, and, ifnecessary, a magnetic material, a fluidizing agent and other additives,using a ball mill or another mechanical mixer, subsequently kneading themixture in a molten state using a hot kneader such as a heat roll,kneader or extruder, cooling and solidifying the mixture, thenpulverizing the solid and classifying the resulting particles by size.

[0068] Other applicable methods include the method in which the startingmaterials other than the binder resin are dispersed in a binder resinsolution and subsequently spray dried to yield the desired toner, andthe polymerization method in which a given set of starting materials aremixed in a monomer to constitute a binder resin to yield an emulsifiedsuspension, which is then polymerized to yield the desired toner.

[0069] When the toner of the present invention for developingelectrostatic images is used as a two-component developer, developmentcan be achieved by the two-component magnetic brush developing processor the like using the toner of the present invention in mixture withcarrier powder.

[0070] Usable carrier is not particularly limited. Any commonly knowncarrier can be used. Examples of usable carriers include iron powder,nickel powder, ferrite powder and glass beads about 50 to 200 μm inparticle diameter, and such materials as coated with acrylate copolymer,styrene-acrylate copolymer, styrene-methacrylate copolymer, siliconeresin, polyamide resin, ethylene fluoride resin or the like.

[0071] When the toner of the present invention for developingelectrostatic images is used as a one-component developer, anappropriate amount of a fine powder of a ferromagnetic material, such asiron powder, nickel powder or ferrite powder, may be added and dispersedin preparing the toner as described above.

[0072] On the other hand, by adding the charge control agent of thepresent invention to a resin powder paint for electrostatic painting,the charge of the powder paint can be controlled or enhanced. Because aresin powder paint for electrostatic painting that contains the chargecontrol agent of the present invention is excellent in heat resistanceand good in charge enhancing characteristic, it exhibits high paintadhesion efficiency even without recovery and reuse (i.e. recycled use).Painting using the powder paint can be achieved using an electrostaticpowder painting method such as the corona application method, thefrictional charging method or the hybrid method.

[0073] It is also possible to obtain a frictional charge providingelement capable of providing a charge for a toner for developingelectrostatic images, by coating the surface of a carrier, a cylindricalsleeve of a transportation member for a toner, a doctor blade or thelike, with the monoazo metal complex compound containing composition ofthe present invention as a charge control agent, by dipping, spraying,brush application or the like.

[0074] This frictional charge providing element is capable of producingtoner images of high quality comparable to that of initial images evenafter continuous copying because the monoazo metal complex compoundcontaining composition used stably provides a positive charge for atoner. In addition, this frictional charge providing element may alsocomprise a small amount of an auxiliary positive charge providing agent.

[0075] The monoazo metal complex compound containing composition of thepresent invention is used as an absorbent dye for ultraviolet light,visible light, infrared light, and the like. Specifically, it is used indyes (coloring agents) for writing inks, recording inks (includinginkjet inks), leather, plastics, etc, near infrared absorbent dyes.Because the monoazo metal complex compound containing composition of thepresent invention possesses a practically satisfactory coloringcharacteristic for a coloring agent, and because it is of high puritywith impurity substances removed previously, its solubility is verystable, it exhibits almost no transfer, such as bleeding due to impuritysubstances, its heat resistance and light fastness are excellent, andits fading is slow with almost no hue change during color fading.

[0076] In addition, inks and dense solutions containing the monoazometal complex compound containing composition of the present inventionas a dye are excellently stable over time with no time-relatedthickening or dye deposition because the dye dissolution stability isgood so that crystal deposition or dye association due to impuritysubstances does not occur.

[0077] Furthermore, the monoazo metal complex compound containingcomposition of the present invention is useful as, for example, a dyefor coloring a thermoplastic resin composition. When it is formulated asa coloring agent for plastics, especially as a coloring agent forplastic products used during a long time of direct contact with thehuman skin, e.g., plastic eyeglass frames, it is excellently harmless tothe human body with almost no skin sensitizing potential as exhibited byconventional azo disperse dyes.

[0078] In addition, the colored thermoplastic resin composition of thepresent invention is excellent in uniform colorability, light fastnessand heat resistance, and its molded product has improved gloss andappearance, because the monoazo metal complex compound containingcomposition of the present invention used as the coloring agent is ofhigh purity and is good in dispersibility and/or solubility inthermoplastic resins.

[0079] The following crystalline thermoplastic resins, for example, canbe used for the colored thermoplastic resin composition of the presentinvention. Specifically, there may be mentioned polyamide resin,polyethylene resin, polypropylene resin, polyester resin (polyethyleneterephthalate resin, polybutylene terephthalate resin, etc.),polyphenylene sulfide resin and polyether ether ketone resin. Of thesethermoplastic resins, polyamide resin, polyester resin (polyethyleneterephthalate resin, polybutylene terephthalate resin, etc.) andpolyphenylene sulfide resin are preferred. These thermoplastic resinsmay be used singly or in combination of two or more kinds. In addition,as other examples of thermoplastic resins that can be used for thecolored thermoplastic resin composition of the present invention, theremay be mentioned copolymers or mixtures mainly comprising thesepolymers; thermoplastic resins prepared by formulating an elastomer suchas rubber or rubber-like resin therein; and polymer alloys containingnot less than 10% by weight of these resins.

[0080] Examples of such polyamide resins include nylon 6, nylon 66,nylon 46, nylon 11, nylon 12, nylon 69, nylon 610, nylon 612, nylon 96,amorphous nylon, nylon RIM, nylon MIX 6, and copolymers of two or morethereof, such as nylon 6/66 copolymer, nylon 6/66/610 copolymer, nylon6/66/11/12 copolymer, and crystalline nylon/amorphous nylon copolymer.In addition, the polyamide resin for the present invention may be apolymer alloy of polyamide resin and another synthetic resin. Examplesof such alloys include polyamide/polyester alloy,polyamide/polyphenylene oxide alloy, polyamide/polycarbonate alloy,polyamide/polyolefin alloy, polyamide/styrene/acrylonitrile alloy,polyamide/acrylic acid ester alloy, and polyamide/silicone alloy. Thesepolyamide resins may be used singly or in combination of two or morekinds.

[0081] The colored thermoplastic resin composition of the presentinvention may contain appropriate amounts of various fibrous reinforcingmaterials according to its use and purpose. Any fibrous reinforcingmaterial can be used for the colored thermoplastic resin composition andfiber-reinforced colored thermoplastic resin molded product of thepresent invention, as long as it can be used to reinforce conventionalsynthetic resins. Examples of such fibrous reinforcing materials includeglass fiber, carbon fiber and various organic fibers. In the case ofglass fiber, for example, its content is preferably set at 5 to 120% byweight relative to 100% by weight of the thermoplastic resin (preferablycrystalline thermoplastic resin). If the glass fiber content is under 5%by weight, satisfactory reinforcing effect is difficult to achieve withthe glass fiber; if the glass fiber content exceeds 120% by weight, themoldability tends to decrease. The glass fiber content is preferably 10to 60% by weight, particularly preferably 20 to 50% by weight.

[0082] The colored thermoplastic resin composition of the presentinvention and the fiber-reinforced colored thermoplastic resin moldedproduct of the present invention may be formulated with various commonlyknown additives to confer desired characteristics according to theobjective. Examples of such additives include auxiliary colorants,modifiers, ultraviolet absorbents or light stabilizers, antioxidants,antibacterial/antifungal agents, flame retarders, inorganic fillers,dispersing agents, stabilizers, plasticizers, antistatic agents andelastomers for improved impact resistance.

[0083] Auxiliary colorants include, for example, inorganic pigments,organic pigments or organic dyes used in small amounts to enhance thecoloring power, to improve the heat resistance and light fastness, or toadjust the color tone.

[0084] Examples of modifiers include silicon compounds such asamino-modified silicone oil and alkyl-modified silicone oil, and waxes.

[0085] Examples of ultraviolet absorbents or light stabilizers includebenzotriazole compounds, benzophenone compounds, salicylate compounds,cyanoacrylate compounds, benzoate compounds, oxalide compounds, hinderedamine compounds and niccolates.

[0086] Examples of antioxidants include phenol compounds, phosphoruscompounds, sulfur compounds and thioether compounds.

[0087] Examples of antibacterial/antifungal agents include2-(4′-thiazolyl)-benzimidazole, 10,10′-oxybisphenoxarsine,N-(fluorodichloromethylthio)phthalimide andbis(2-pyridylthio-1-oxide)zinc.

[0088] Examples of flame retarders include halogen containing compoundssuch as tetrabromobisphenol A derivatives, hexabromodiphenyl ether andtetrabromophthalic anhydride; phosphorus containing compounds such astriphenyl phosphate, triphenyl phosphite, red phosphorus and ammoniumpolyphosphate; nitrogen containing compounds such as urea and guanidine;silicon containing compounds such as silicone oil, organic silane andaluminum silicate; and antimony compounds such as antimony trioxide andantimony phosphate.

[0089] Examples of inorganic fillers include glass flake, glass beads,silica, quartz, amorphous silicic acid, talc, magnesium carbonate,calcium carbonate, alumina, metal powder, kaolin, calcium silicate, micaand wollastonite.

[0090] The colored thermoplastic resin composition of the presentinvention can be prepared by formulating the starting materials by anoptionally chosen method of formulation. Normally, it is preferable tomix these components as uniformly as possible. For example, a coloredthermoplastic resin composition can be prepared by uniformly mixing allstarting materials in a mechanical mixer such as a blender, a kneader, abanbury mixer, a roll or an extruder. Alternatively, it can be obtainedby mixing some starting materials in a mechanical mixer, andsubsequently adding the remaining components and uniformly mixing them.It can also be obtained as colored grains (colored pellets) by kneadingthe starting materials, previously dry blended, in a molten state usinga heated extruder, to obtain a uniform mixture, extruding the mixtureinto a needle form, and subsequently cutting it into pieces of desiredlength.

[0091] In addition, a master batch of the colored thermoplastic resincomposition of the present invention can be obtained by an optionallychosen method. For example, it can be obtained by mixing a thermoplasticresin (preferably a crystalline thermoplastic resin) as the master batchbase, in a powder or pellet form, and the monoazo metal complex compoundcontaining composition of the present invention as a coloring agent, ina mechanical mixer such as a tumbler or a super-mixer, and pelletizingor coarsely granulating the mixture by the hot melt method using anextruder, a batch kneader, a roll kneader, or the like. A master batchcan also be obtained by adding the monoazo metal complex compoundcontaining composition of the present invention as a coloring agent to athermoplastic resin for master batch remaining in a molten state aftersynthesis, then removing the solvent.

[0092] The colored thermoplastic resin composition of the presentinvention can be molded by various procedures in common use. Forexample, it can be molded from colored pellets using a molding machinesuch as an extruder, an injection molding machine or a roll mill. Inaddition, it can be molded by mixing in an appropriate mixer athermoplastic resin, in a pellet or powder form, the monoazo metalcomplex compound containing composition of the present invention in apulverized form as a coloring agent, and various additives used asnecessary, and molding this mixture using a molding machine. It is alsopossible to add the monoazo metal complex compound containingcomposition of the present invention as a coloring agent to a monomercontaining an appropriate polymerization catalyst, polymerize thismixture into a desired crystalline thermoplastic resin, and mold thisresin by an appropriate method. Molding can be achieved by any moldingmethods in common use, including injection molding, extrusion molding,compression molding, foaming molding, blow molding, vacuum molding,injection blow molding, rotational molding, calendering and solutioncasting

EXAMPLES

[0093] The present invention is hereinafter described in more detail bymeans of the following examples, which are not to be construed aslimitative. In the description below, “part(s) by weight” is referred toas “part(s)”.

[0094] Examples 1 and 2 and Comparative Examples 1 and 2 concern theproduction of the monoazo metal complex compound containing compositionof the present invention.

Example 1

[0095] (a) Synthesis of monoazo dye Water 300 ml Hydrochloric acid 20.0g 4-chloro-2-aminophenol 28.6 g

[0096] After an aqueous solution comprising the above ingredients wascooled to 5□, a solution of 14.0 g of sodium nitrite in 60 ml of waterwas added to the solution drop by drop over a period of 30 minutes. Thismixture was stirred at 5 to 15□ for 1 hour, after which the reactionmixture was filtered, to yield an aqueous solution of the diazonium saltof 4-chloro-2-aminophenol (solution A). Water 400 ml Sodium hydroxide14.0 g 2-naphthol 28.8 g

[0097] Subsequently, the aforementioned solution A was added drop bydrop over a period of 40 minutes to an aqueous solution of theingredients shown above, after which this mixture was stirred for 3hours. The precipitated reaction product was collected by filtration,washed with water, and dried at 100□, to yield 62.0 g of1-(5-chloro-2-hydroxyphenyl)azo-2-hydroxynaphthalene (monoazo dye). (b)Synthesis of monoazo metal complex compound Monoazo dye obtained in (a)62.0 g Chromium formate 19.2 g Ethylene glycol monoethyl ether 200 g

[0098] After the above ingredients were mixed and stirred at 130□ for 6hours, this mixture was cooled to 90□, and the reaction mixture wasdispersed in an aqueous solution of 15 g of hydrochloric acid in 200 mlof water. The solid was separated from this dispersion by filtration andwashed with 1200 ml of water, after which it was dried at 100 □. Theblack product obtained was milled to yield 60 g of a non-purifiedmonoazo metal complex compound (composition containing a monoazo metalcomplex compound).

[0099] (c) Purification Process

[0100] 60 g of the non-purified monoazo metal complex compound(composition containing a monoazo metal complex compound) was dispersedin 120 g of methanol and stirred at 63□ for 1 hour, after which it wascooled to 30□ and filtered through Toyo Filter Paper No. 2. The wet cakeobtained was further washed with 20 g of methanol on filter paper anddried at 50□ under reduced pressure to yield 56.4 g of a purified blackproduct (monoazo metal complex compound containing composition 1).

[0101] The purified monoazo metal complex compound (monoazo metalcomplex compound containing composition 1) was analyzed by highperformance liquid chromatography and its purity was determined to be94.3% (high performance liquid chromatography data presented in FIG. 1).The incidence of skin sensitization in a skin sensitization potentialtest based on the maximization method was 10%. A TG/DTA chart of thepurified monoazo metal complex compound (monoazo metal complex compoundcontaining composition 1) is shown in FIG. 2.

High Performance Liquid Chromatography (HPLC) Operating Conditions (theSame Applies to the High Performance Liquid Chromatography AnalysisDescribed Below)

[0102] Column: L-column ODS (produced by the Chemicals Inspection &Testing Institute, Japan)

[0103] Eluent: Mixture of 80 parts by volume of acetonitrile, 1 part byvolume of triethylamine, 3 parts by volume of acetic acid, and 16 partsby volume of water

[0104] Flow rate: 1.0 ml/min

[0105] Column temperature: 45□

[0106] Measuring wavelength: 313 nm

[0107] Injection volume: 10 μl

[0108] Sample preparation: 10 mg/10 cc (80 parts by volume ofacetonitrile and 20 parts by volume of water)

Example 2

[0109] Monoazo dye obtained in Example 1 (a) 62.0 g Chromium formate19.2 g Ethylene glycol monoethyl ether 200 ml

[0110] After the above ingredients were mixed and stirred at 130□ for 6hours, this mixture was cooled to 30□. The solid was separated from thereaction mixture by filtration and washed with 100 ml of water on filterpaper, after which its wet cake was dispersed again in an aqueoussolution of 15 g of hydrochloric acid in 200 ml of water and stirred for1 hour. Subsequently, the solid was again separated by filtration andwashed with 1200 ml of water, after which it was dried at 100□ andmilled to yield 56.6 g of a purified black product (monoazo metalcomplex compound containing composition 2).

[0111] The purified monoazo metal complex compound (monoazo metalcomplex compound containing composition 2) was analyzed by highperformance liquid chromatography and its purity was determined to be95.9%. The incidence of skin sensitization in a skin sensitizationpotential test based on the maximization method was 10%.

[0112] Comparative Example 1 Monoazo dye obtained in Example 1 (a) 62.0g Chromium formate 19.2 g Ethylene glycol monoethyl ether 200 ml

[0113] After the above ingredients were mixed and stirred at 130□ for 6hours, this mixture was cooled to 90□. This reaction mixture wasdispersed in an aqueous solution of 15 g of hydrochloric acid in 200 mlof water. The solid was separated from this dispersion by filtration andwashed with 1200 ml of water, after which it was dried at 100□ andmilled, to yield 60 g of a non-purified black product (compositioncontaining a monoazo metal complex compound).

[0114] This non-purified monoazo metal complex compound (compositioncontaining a monoazo metal complex compound) was analyzed by highperformance liquid chromatography, and its purity was determined to be82.8% (high performance liquid chromatography data presented in FIG. 3).The incidence of skin sensitization in a skin sensitization potentialtest based on the maximization method was 90%.

Comparative Example 2

[0115] 50 g of the non-purified monoazo metal complex compound(composition containing a monoazo metal complex compound) obtained inComparative Example 1 was dispersed in 100 g of methanol and stirredunder refluxing at 63□ for 1 hour, after which it was cooled to 30□ andfiltered through Toyo Filter Paper No. 2. The entire portion of thefiltrate obtained was dispersed in an aqueous solution of 15 g ofhydrochloric acid in 200 ml water. The solid was separated from thedispersion by filtration and washed with 1200 ml of water, after whichit was dried at 100□ and milled, to yield 3.4 g of a black powder(composition containing a monoazo metal complex compound). This blackpowder was analyzed by high performance liquid chromatography, and itspurity was determined to be 27.8% (high performance liquidchromatography data presented in FIG. 4). The incidence of skinsensitization in a skin sensitization potential test based on themaximization method was 100%. A TG/DTA chart of this black powder isshown in FIG. 5.

[0116] The sensitizing potentials, purities, X-ray diffraction profiles,and mean particle diameters of the substances obtained in Examples 1 and2 and Comparative Examples 1 and 2 are shown in Table 1. TABLE 1Sensitization by the maximization method Number of samples withsensitization Percent HPLC- signs found/number of Incidenc determinedX-ray Mean particle dia samples analyzed (%) purity (%) Diffractionmeter (μm) Example 1 1/10 10 94.2 Crystalline 6.74 Example 2 1/10 1095.9 Crystalline 6.28 Comparative Ex 9/10 90 82.8 Crystalline 6.23 ample1 Comparative Ex 10/10  100 27.8 Amorphous 6.50 ample 2

[0117] Examples 3 and 4 and Comparative Examples 3 and 4 concern tonersfor developing electrostatic images that incorporate the monoazo metalcomplex compound containing composition of the present invention as acharge control agent.

Example 3

[0118] Styrene-acrylic copolymer resin (produced by Mitsui Chemical Co.,Ltd., trade name: CPR600B) . . . 100 parts

[0119] Carbon Black (produced by Mitsubishi Chemical Co., Ltd., tradename: MA-100) . . . 7 parts

[0120] Low polymer polypropylene (produced by Sanyo Kasei Co., Ltd.,trade name: Biscal 550P) . . . 3 parts

[0121] Charge control agent (monoazo metal complex compound containingcomposition 1) . . . 3 parts

[0122] The above ingredients were uniformly pre-mixed using a high-speedmixer to yield a premix, which was then kneaded in a molten state usinga heat roll, cooled and thereafter roughly milled using a vibrationmill. The rough milling product obtained was finely pulverized using anair jet mill equipped with a mechanical classifier to yield a blacktoner 5 to 15 μm in particle diameter.

[0123] Five parts of this toner was admixed with 95 parts of an ironpowder carrier (produced by Powdertech, TEFV200/300) to yield adeveloper.

[0124] When this toner was used to repeatedly form images, the chargerise profile, charge stability and sustainability were good, the imagedensity was stable from the initial time to completion of continuouscopying, and high-quality black images with no fogging etc. wereobtained.

[0125] After this developer was stirred for a preset time, the amount ofblowoff charges was determined using a blowoff charge tester (producedby Toshiba Chemical). The amount of saturated charges was determined tobe −55.7 μC/g. The results of determination are shown in Table 2 andFIG. 6.

Example 4

[0126] In the same manner as in Example 3, except that the chargecontrol agent used in Example 3 was replaced with the monoazo metalcomplex compound containing composition 2 obtained in Example 2, a tonerwas obtained, a developer was prepared, and the amount of blowoffcharges was determined. The amount of saturated charges was determinedto be −54.6 μC/g. The results of determination are shown in Table 2 andFIG. 6.

Comparative Example 3

[0127] In the same manner as in Example 3, except that the chargecontrol agent used in Example 3 was replaced with the non-purifiedmonoazo metal complex compound (composition containing a monoazo metalcomplex compound) obtained in Comparative Example 1, a toner wasobtained and a developer was prepared. When this developer was used torepeatedly form images, the charge rise profile, charge stability, andsustainability were good, the image density was stable from the initialtime to completion of continuous copying, and high-quality black imageswith no fogging etc. were obtained. When the amount of blowoff chargeswas determined in the same manner as in Example 3, the amount ofsaturated charges was determined to be −54.1 μC/g. The results ofdetermination are shown in Table 2 and FIG. 6.

Comparative Example 4

[0128] In the same manner as in Example 3, except that the chargecontrol agent used in Example 3 was replaced with the methanol-solubleblack powder (composition containing a monoazo metal complex compound)obtained in Comparative Example 2, a toner was obtained and a developerwas prepared. When this developer was used to repeatedly form images,fogging occurred and no satisfactory images were obtained with densityreduction as compared to initial images. When the amount of blowoffcharges was determined in the same manner as in Example 3, the amount ofsaturated charges was determined to be −38.0 μC/g. The results ofdetermination are shown in Table 2 and FIG. 6. TABLE 2 Amount ofsaturated charges after toner Toner Charge control agent formation(−μC/g) Example 3 Example 1 55.7 Example 4 Example 2 54.6 ComparativeExample 3 Comparative Example 1 54.1 Comparative Example 4 ComparativeExample 2 38.0

[0129] Examples 5 and 7 and Comparative Examples 5 and 6 concern coloredpolyamide resin compositions that incorporate the monoazo metal complexcompound containing composition of the present invention as a dye.

Example 5

[0130] 1000 g of a polyamide resin (produced by Dupont, trade name:Zytel 101L-NC10) and 30 g of the monoazo metal complex compoundcontaining composition 1 of Example 1 (black dye as a coloring agent)were placed in a stainless steel tumbler and stirred vigorously for 20minutes.

[0131] This mixture was kneaded in a molten state at 300□ using a venttype extruding machine (produced by Enpura Sangyo, trade name: E30SV)and treated by a conventional method to yield colored pellets, whichwere vacuum-dried at 120□ for 6 hours.

[0132] After pellet drying, a test piece was prepared at 280 to 300 □ byan ordinary method using an injection molding machine (produced byKawaguchi Tekko, trade name: KM-50C). A reddish black molded test piecewith good compatibility between the resin and the dye [48×86×3 (mm)] wasobtained.

[0133] The results of evaluation and measurement of the appearance andsurface gloss of this molded test piece are shown in Table 3.

[0134] (1) Appearance and Surface Gloss (visual evaluation of coloringcondition)

[0135] The test piece was examined visually under standard light C (JISL0804) to evaluate its coloring condition.

Evaluation Criteria for Coloring

[0136] □: Uniformly and vividly colored and rich in gloss.

[0137] ◯: Uniformly colored and glossy.

[0138] □: Partially ununiformly colored and partially glossless.

[0139] x: Totally ununiformly colored and glossless.

[0140] (2) Light Fastness Test and Evaluation

[0141] Using the Sunshine xenon long-life weather meter (produced byShimadzu Corporation, trade name: XW-1200A), the test piece was exposedto light for 200 hours in a cycle of the 006 test conditions (phases 1and 2 repeated under the conditions shown below), after which its gradewas determined on the BLUE SCALE (JIS L0841 method).

[0142] In general, test pieces rated lower are judged to have greaterdiscoloration and fading. Light fastness test conditions with Sunshinexenon long-life weather meter [Setting item] [Phase 1] [Phase 2]Irradiance (Wm/2) (E) 70 70 Black standard temperature (□) 63 50Rainfall test No Yes Humidity (%) 60 — Time (min) 120  18

[0143] 1000 g of a thermoplastic resin and 0.5 g of a coloring agentwere placed in a stainless steel tumbler and stirred vigorously for 1hour. This mixture was kneaded in a molten state using a vent typeextruding machine and treated by a conventional method to yield coloredpellets. After these colored pellets were vacuum-dried at 120□ for 6hours, a molded test piece was prepared with the pellets by an ordinarymethod using an injection molding machine, and this molded test piecewas used as the standard test piece. Separately, the colored pelletswere kept at 310□ for 5 minutes in an injection molding machine, afterwhich a molded test piece was prepared. This molded test piece and thestandard molded test piece were compared on the BLUE SCALE (JIS L0841)to determine its grade. In general, test pieces rated lower are judgedto have greater discoloration and fading.

Example 6

[0144] In the same manner as in Example 5, except that the monoazo metalcomplex compound containing composition 1 was replaced with 30 g of themonoazo metal complex compound containing composition 2 of Example 2(black dye as a coloring agent), a uniformly colored reddish blackmolded test piece [48×86×3 (mm)] with good appearance and surface glosswas obtained.

[0145] This molded test piece was tested and evaluated forappearance/surface gloss, light fastness, and heat resistance in thesame manner as in Example 5. The results are shown in Table 3.

Example 7

[0146] 100 g of glass-reinforced nylon 66 (fiber-reinforced polyamideresin with a mixing ratio by weight of polyamide resin:glassfiber=67:33, produced by Dupont, trade name: 70G33L) and 30 g of themonoazo metal complex compound containing composition 1 of Example 1(black dye as a coloring agent) were placed in a stainless steel tumblerand stirred vigorously for 20 minutes.

[0147] This mixture was kneaded in a molten state at 300□ using a venttype extruding machine (produced by Enpura Sangyo, trade name: E30SV)and treated by a conventional method to yield colored pellets, whichwere vacuum-dried at 120□ for 6 hours.

[0148] After pellet drying, a test piece was prepared at 280 to 300□with the pellets by an ordinary method using an injection-moldingmachine (produced by Kawaguchi Tekko, trade name: KM50-C). A reddishblack molded test piece with good compatibility between the resin andthe dye [48×86×3 (mm)] was obtained.

Comparative Example 5

[0149] In the same manner as in Example 5, except that the monoazo metalcomplex compound containing composition 1 in Example 5 was replaced with30 g of the non-purified monoazo metal complex compound (compositioncontaining a monoazo metal complex compound) obtained in ComparativeExample 1, a uniformly colored reddish black molded test piece [48×86×3(mm)] was obtained.

[0150] This molded test piece was tested and evaluated forappearance/surface gloss, light fastness, and heat resistance in thesame manner as in Example 5. The results are shown in Table 3.

Comparative Example 6

[0151] In the same manner as in Example 5, except that the monoazo metalcomplex compound containing composition 1 in Example 5 was replaced withthe methanol-soluble black powder obtained in Comparative Example 2(composition containing a monoazo metal complex compound), anununiformly colored red molded test piece [48×86×3 (mm)] was obtained.

[0152] This molded test piece was tested and evaluated forappearance/surface gloss, light fastness, and heat resistance in thesame manner as in Example 5. The results are shown in Table 3. TABLE 3Light Heat Appearance/surface fastness resistance Coloring agent glosstest test Example 5 Example 1 □ Grade 8 Grade 7 Example 6 Example 2 □Grade 8 Grade 7 Comparative Comparative ∘ Grade 6 Grade 5 Example 5Example 1 Comparative Comparative x Grade 3 Grade 3 Example 6 Example 2

What is claimed is:
 1. Monoazo metal complex compound containingcomposition, the incidence of skin sensitization in a skin sensitizationpotential test of said composition being not more than 20%.
 2. Monoazometal complex compound containing composition of claim 1 wherein saidskin sensitization potential test is a skin sensitization potential testbased on the maximization method.
 3. Monoazo metal complex compoundcontaining composition of claim 1 wherein the purity of said monoazometal complex compound is not less than 90% as determined by highperformance liquid chromatography.
 4. Monoazo metal complex compoundcontaining composition of claim 2 wherein the purity of said monoazometal complex compound is not less than 90% as determined by highperformance liquid chromatography.
 5. Monoazo metal complex compoundcontaining composition of any of claims 1, 2, 3 or 4 wherein saidmonoazo metal complex compound is a compound of the following formula(1):

wherein each of R¹ through R⁴ and R⁶ independently represents a hydrogenatom, a normal or branched alkyl group having 1 to 18 carbon atoms, anormal or branched alkenyl group having 2 to 18 carbon atoms, asulfonamide group, a mesyl group, a sulfonic acid group, a hydroxygroup, an alkoxy group having 1 to 18 carbon atoms, an acetylaminogroup, a benzoylamino group, a halogen atom, or —COO—R⁷; R⁷ represents anormal or branched alkyl group having 1 to 18 carbon atoms or an arylgroup having 6 to 18 carbon atoms; R⁵ represents a hydrogen atom, ahalogen atom, a nitro group, a carboxyl group, a normal or branchedalkyl group having 1 to 18 carbon atoms, an alkenyl group having 2 to 18carbon atoms, an alkoxy group having 1 to 18 carbon atoms, an aryl grouphaving 6 to 18 carbon atoms, —COO—R⁸ or

R⁸ represents a normal or branched alkyl group having 1 to 18 carbonatoms or an aryl group having 6 to 18 carbon atoms; Y represents ahydrogen atom, a normal or branched alkyl group having 1 to 8 carbonatoms, an alkoxy group having 1 to 5 carbon atoms, a nitro group, or ahalogen atom; m represents an integer from 1 to 3; M represents adivalent or trivalent metal; p represents 1 or 2; (A)^(q+) representsH⁺, NH₄ ⁺, a cation based on an alkali metal, a cation based on anorganic amine, or a quaternary organic ammonium ion; q represents 1 or2; and X represents 1 or
 2. 6. Monoazo metal complex compound containingcomposition of claim 5 wherein R² in Formula (1) above is Cl; each of R¹and R³ through R⁵ is a hydrogen atom; R⁶ is a hydrogen atom or a normalor branched alkyl group having 1 to 18 carbon atoms; M is Cr, Fe, or Cu;and (A)^(q+) is H⁺.
 7. Method for producing a monoazo metal complexcompound containing composition which comprises a step for removingimpurity substances using an alcoholic organic solvent, the incidence ofskin sensitization in a skin sensitization potential test of saidcomposition being not more than 20%.
 8. Method for producing the monoazometal complex compound containing composition of claim 7 wherein saidskin sensitization potential test is a skin sensitization potential testbased on the maximization method.
 9. Method for producing the monoazometal complex compound containing composition of claim 7 wherein thepurity of said monoazo metal complex compound is not less than 90% asdetermined by high performance liquid chromatography.
 10. Method forproducing the monoazo metal complex compound containing composition ofclaim 8 wherein the purity of said monoazo metal complex compound is notless than 90% as determined by high performance liquid chromatography.11. Method for producing the monoazo metal complex compound containingcomposition of claim 7, 8, 9 or 10 wherein said alcoholic organicsolvent is one member or a mixture of two or more members selected fromthe group consisting of methanol, ethanol, 1-propanol, 2-propanol,n-butanol, ethylene glycol, propylene glycol monomethyl ether andethylene glycol monoethyl ether.
 12. Method for producing a monoazometal complex compound containing composition which comprises a step forsynthesizing a monoazo metal complex compound in an alcoholic organicsolvent, and a step for removing impurity substances from the product ofthe synthetic step using an alcoholic organic solvent, the incidence ofskin sensitization in a skin sensitization potential test of saidcomposition being not more than 20%.
 13. Method for producing themonoazo metal complex compound containing composition of claims 12wherein said skin sensitization potential test is a skin sensitizationpotential test based on the maximization method.
 14. Method forproducing the monoazo metal complex compound containing composition ofclaims 12 wherein the purity of said monoazo metal complex compound isnot less than 90% as determined by high performance liquidchromatography.
 15. Method for producing the monoazo metal complexcompound containing composition of claims 13 wherein the purity of saidmonoazo metal complex compound is not less than 90% as determined byhigh performance liquid chromatography.
 16. Method for producing themonoazo metal complex compound containing composition of claim 12, 13,14 or 15 wherein said alcoholic organic solvent is one member or amixture of two or more members selected from the group consisting ofmethanol, ethanol, 1-propanol, 2-propanol, n-butanol, ethylene glycol,propylene glycol monomethyl ether and ethylene glycol monoethyl ether.17. Method for producing a monoazo metal complex compound containingcomposition which comprises a step for synthesizing a monoazo metalcomplex compound in an alcoholic organic solvent, and a step forremoving impurity substances by directly filtering a reaction mixturecontaining the product obtained by the synthetic step, the incidence ofskin sensitization in a skin sensitization potential test of saidcomposition being not more than 20%.
 18. Method for producing themonoazo metal complex compound containing composition of claims 17wherein said skin sensitization potential test is a skin sensitizationpotential test based on the maximization method.
 19. Method forproducing the monoazo metal complex compound containing composition ofclaims 18 wherein the purity of said monoazo metal complex compound isnot less than 90% as determined by high performance liquidchromatography.
 20. Method for producing the monoazo metal complexcompound containing composition of claims 19 wherein the purity of saidmonoazo metal complex compound is not less than 90% as determined byhigh performance liquid chromatography.
 21. Method for producing themonoazo metal complex compound containing composition of claim 17, 18,19 or 20 wherein said alcoholic organic solvent is one member or amixture of two or more members selected from the group consisting ofmethanol, ethanol, 1-propanol, 2-propanol, n-butanol, ethylene glycol,propylene glycol monomethyl ether and ethylene glycol monoethyl ether.22. Charge control agent comprising a monoazo metal complex compoundcontaining composition, the incidence of skin sensitization in a skinsensitization potential test of said composition being not more than20%.
 23. Toner for developing electrostatic images which contains acharge control agent comprising a monoazo metal complex compoundcontaining composition, the incidence of skin sensitization in a skinsensitization potential test of said composition being not more than20%.
 24. Coloring agent containing the monoazo metal complex compoundcontaining composition, the incidence of skin sensitization in a skinsensitization potential test of said composition being not more than20%.
 25. Colored thermoplastic resin composition containing the monoazometal complex compound containing composition as a coloring agent, theincidence of skin sensitization in a skin sensitization potential testof said composition being not more than 20%.